Chemically Clad Powder

Chemically clad powder is a composite material manufactured by chemically bonding a metallic binder to the surface of hard particles, ensuring a uniform composition and excellent particle integrity. It offers outstanding wear resistance, strong coating adhesion, and reliable performance in thermal spray and hardfacing applications. The powder is widely used to protect industrial components against abrasion, erosion, and corrosion, helping to extend service life in demanding operating environments.

1.High bonding strength with substrate.

2.Superior corrosion and oxidation resistance.

3.High compressive strength and excellent durability.

4.Good thermal stability at elevated temperatures.

5.Excellent flowability for consistent spraying

6.Improves component life and reduces maintenance costs.

Brand	Product Name	AMPERIT	METCO/AMDRY	WOKA	PRAXAIR	PAC
AA-2	NiA182/18		404NS
AA-11T/R	Ni-Graphite 75/25	205	307NS		NI-114	138
AA-12T/R	Ni-Graphite 60/40	200	Durabrade 2211
AA-20	Ni-Mos₂
AA-45	Ni-Al₂O₃ 77/23
AA-50	Ni-WC10/90
AA-56	Ni-WC 16/84
AA-31	Ni-Diatomite 75/25

Brand	Product Name	Temprature	Type	Properties	Application
AA-2	NiA182/18	≤650°C	Chemically Clad	APS	1.Dense , machinable oxidation resistant 2.Self-bonding 3.Exothermic Spraying Process
AA-11T/R	Ni-Graphite 75/25	≤480°C	Chemically Clad	FS	1.Tturbine Compressor abradables 2.For running against nickel alloy & Steel Parts 3. Higher graphite content enhances lubricity
AA-12T/R	Ni-Graphite 60/40	≤480°C	Chemically Clad	FS	1.Tturbine Compressor abradables 2.For running against nickel alloy & Steel Parts 3. Higher graphite content enhances lubricity
AA-20	Ni-Mos₂	≤500°C	Chemically Clad	APS	1.Used for movable sealing parts and grindable sealing rings 2.It can be used low friction material
AA-45	Ni-Al₂O₃ 77/23	≤500°C	Chemically Clad	APS	1.Applied to melting crucible mold surface as protective layer 2.Made porous filter membrane with special properties
AA-50	Ni-WC10/90	≤400°C	Chemically Clad	HVOF	1.Resistance to hamering , erosion , abrasion 2.Higher corosion resistance 3.Suitable for plasma spraying
AA-56	Ni-WC 16/84	≤400°C	Chemically Clad	HVOF	1.Resistance to hamering , erosion , abrasion 2.Higher corosion resistance 3.Suitable for plasma spraying
AA-31	Ni-Diatomite 75/25	≤650°C	Chemically Clad	APS	1.For adorable seal coating , including movable seal parts , low friction material